Polycarbonate (PC)

Compressive Yield Strength

CTE, linear 20°C

Deflection Temperature at 1.8 MPa (264 psi)

Density

Dielectric Constant

Dielectric Strength

Electrical Resistivity

Elongation at Break

Flexural Yield Strength

Hardness, Rockwell R

Izod Impact, Notched

Izod Impact, Unnotched

Max Service Temperature, Air

Melt Flow

Modulus of Elasticity

Specific Heat Capacity

Tensile Strength, Ultimate

Tensile Strength, Yield

Thermal Conductivity

Water Absorption

10100 psi

39 µin/in-°F

266 °F

0.0434 lb/in³

3

671 kV/in

7.00E+16 ohm-cm

97.9 %

13300 psi

120

13.5 ft-lb/in

36.5 ft-lb

266 °F

14.2 g/10 min

334 ksi

0.365 BTU/lb-°F

9280 psi

8990 psi

1.39 BTU-in/hr-ft²-°F

0.17 %