Polycarbonate / ABS (Alloy)
Compressive Yield Strength
CTE, linear 20°C Deflection Temperature at 1.8 MPa (264 psi) Density Dielectric Constant Dielectric Strength Electrical Resistivity Elongation at Break Flexural Yield Strength Hardness, Rockwell R Izod Impact, Notched Izod Impact, Unnotched Max Service Temperature, Air Melt Flow Modulus of Elasticity Specific Heat Capacity Tensile Strength, Ultimate Tensile Strength, Yield Thermal Conductivity Water Absorption |
—