Acetal Homopolymer, Unreinforced (POM)
Compressive Yield Strength
CTE, linear 20°C Deflection Temperature at 1.8 MPa (264 psi) Density Dielectric Constant Dielectric Strength Electrical Resistivity Elongation at Break Flexural Yield Strength Hardness, Rockwell R Izod Impact, Notched Izod Impact, Unnotched Max Service Temperature, Air Melt Flow Modulus of Elasticity Specific Heat Capacity Tensile Strength, Ultimate Tensile Strength, Yield Thermal Conductivity Water Absorption |
16000 psi
61.1 µin/in-°F 248 °F 0.0509 lb/in³ 3.7 462 kV/in 7.00E+14 ohm-cm 48.3 % 13900 psi 120 2.06 ft-lb/in 35 ft-lb 248 °F 12.6 g/10 min 435 ksi 0.34 BTU/lb-°F 9530 psi 9410 psi 2.57 BTU-in/hr-ft²-°F 0.25 % |